比利時索爾維 TECHNYL B 216 BLACK 3N PA66/6 脫模性能良好

供應 比利時索爾維 TECHNYL B 216 BLACK 3N PA66/6 TECHNYL? B 216 BLACK 3NPolyamide 66/6 CopolymerSolvay Engineering Plastics產品說明：TECHNYL? B 216 Black 3N is an unreinforced copolyamide 66/6, medium viscosity, for injection moulding. This grade offers an excellent combination between impact resistance, rigidity, thermal resistance and surface appearance.物性信息：基本信息黃卡編號E特性良好的流動性脫模性能良好優良外觀用途工業應用汽車領域的應用通用消費品應用領域機構評級EC 1907/2006 (REACH)RoHS 合規性RoHS 合規外觀黑色灰色自然色形式粒子加工方法注射成型樹脂ID (ISO 1043)PA66/6物理性能干燥調節后的單位制測試方法密度1.14--g/cm3ISO 1183/A吸水率 (23°C, 24 hr)1.6--%ISO 62機械性能干燥調節后的單位制測試方法拉伸模量 (23°C)30001100MPaISO 527-2/1A拉伸應力ISO 527-2/1A     屈服, 23°C85.050.0MPaISO 527-2/1A     斷裂, 23°C75.060.0MPaISO 527-2/1A拉伸應變ISO 527-2     屈服, 23°C3.625%ISO 527-2     斷裂, 23°C30--%ISO 527-2彎曲模量 (23°C)30001200MPaISO 178彎曲應力 (23°C)12550.0MPaISO 178沖擊性能干燥調節后的單位制測試方法簡支梁缺口沖擊強度 (23°C)5.016kJ/m2ISO 179/1eA簡支梁無缺口沖擊強度 (23°C)無斷裂--ISO 179/1eU懸壁梁缺口沖擊強度 (23°C)5.016kJ/m2ISO 180熱性能干燥調節后的單位制測試方法熱變形溫度 (1.8 MPa, 未退火)67.0--°CISO 75-2/Af熔融溫度242--°CISO 11357-3電氣性能干燥調節后的單位制測試方法表面電阻率1.0E+151.0E+14ohmsIEC 60093體積電阻率1.0E+151.0E+15ohms·cmIEC 60093介電強度 (2.00 mm)2624kV/mmIEC 60243-1相對電容率3.003.20IEC 60250耗散因數0.0300.10IEC 60250漏電起痕指數IEC 60112     解決方案 A600600VIEC 60112     解決方案 B575--VIEC 60112可燃性干燥調節后的單位制測試方法UL 阻燃等級UL 94     1.6 mmHB--UL 94     3.2 mmV-2--UL 94極限氧指數24--%ISO 4589-2注射干燥單位制干燥溫度80°C建議的最大水分含量0.20%料筒后部溫度250 到 260°C料筒中部溫度255 到 265°C料筒前部溫度265 到 275°C模具溫度60 到 80°C注射說明The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying e, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design