UV DicingTape:No.6360-25
High adhesion
Feature:
?Non-PVC backing is used
?High-Pressure mercury lamp or black light can be used as lightsource
? Isotropicperformance at expanding process
Property:
| Item No. | No.6360-25 | ||||||||||||||
| Color | Tape(PO) | Translucent | |||||||||||||
| Liner | Transparent | ||||||||||||||
| Thickness（um) Liner:38um | Backing | 150 | |||||||||||||
| Adhesive | 10 | ||||||||||||||
| Peelstrength ［N/10mm］ （）:After UV | SUS | 3.40(0.22) | |||||||||||||
| Glass | 3.80(0.23) | ||||||||||||||
| SI wafer | 3.80(0.23) | ||||||||||||||
| Holding Power | 40℃/24hour | ＜ 0.1mm | |||||||||||||
| Tensile Strength (Before UV) (TD/MD）（N/10㎜） | 30/30 | ||||||||||||||
| Elongation (Before UV) （TD/MD）（％/10㎜） | 910/840 | ||||||||||||||
?UV irradiation condition ： High-pressure mercury lamp, 75mW/cm2at 365nm, for 4 sec （300mJ/cm2)
?Peel Strength (90o Peel)： Pass the 2kg roller in each directionat a rate of 300mm/min. Aging time ; 20min. Rate of peel ;300mm/min.
?Holding power ： Pass the 2kg roller in each direction ata rate of 300mm/min. Load ; 1kg/25㎜×25㎜
?TD：Transverse Direction, MD：Machine Direction