Hostaform? LX90Z XAP2 ?
Acetal (POM) Copolymer
Celanese Corporation
產品說明：
Preliminary Data Sheet
Hostaform? acetal copolymer grade LX90Z XAP2 ? is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform? LX90Z XAP2 ? has lower volatile emissions as required for some automotive interiors.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
Low Emission Performance [VDA-275] <5 PPM
物性信息：
| 基本信息 | |
|---|---|
| 添加劑 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合規性 |
|
| 外觀 |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 密度 | 1.43 | g/cm3 | ISO 1183 |
| 溶化體積流率（MVR） (190°C/2.16 kg) | 8.00 | cm3/10min | ISO 1133 |
| 收縮率 | ISO 294-4 | ||
| 垂直流動方向 | 1.4 | % | ISO 294-4 |
| 流動方向 | 2.3 | % | ISO 294-4 |
| 吸水率 (飽和, 23°C) | 0.75 | % | ISO 62 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 拉伸模量 | 2700 | MPa | ISO 527-2/1A/1 |
| 拉伸應力 (屈服) | 54.0 | MPa | ISO 527-2/1A/50 |
| 拉伸應變 (屈服) | 8.0 | % | ISO 527-2/1A/50 |
| 彎曲模量 (23°C) | 2900 | MPa | ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 簡支梁缺口沖擊強度 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 4.0 | kJ/m2 | ISO 179/1eA |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 熱變形溫度 | |||
| 0.45 MPa, 未退火 | 147 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 90.0 | °C | ISO 75-2/A |
| 熔融溫度 1 | 166 | °C | ISO 11357-3 |
| 線形熱膨脹系數 | ISO 11359-2 | ||
| 流動 | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| 橫向 | 1.0E-4 | cm/cm/°C | ISO 11359-2 |