Acetal (POM) Copolymer
Celanese Corporation
產品說明：
Hostaform? acetal copolymer grade MT8F02 is a special grade developed for medical industry applications containing low residual monomers. Hostaform? MT8F02 is a standard flow high level polytetrafluoroethylene filled (PTFE) product designed for use in wear applications against plastics, metal, glass or ceramic mating surfaces where silicone lubricants can not be tolerated.
物性信息：
| 基本信息 | |
|---|---|
| 添加劑 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合規性 |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 密度 | 1.52 | g/cm3 | ISO 1183 |
| 溶化體積流率（MVR） (190°C/2.16 kg) | 6.00 | cm3/10min | ISO 1133 |
| 收縮率 | ISO 294-4 | ||
| 垂直流動方向 | 1.7 | % | ISO 294-4 |
| 流動方向 | 2.0 | % | ISO 294-4 |
| 吸水率 (飽和, 23°C) | 0.20 | % | ISO 62 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 拉伸模量 | 2500 | MPa | ISO 527-2/1A/1 |
| 拉伸應力 (屈服) | 48.0 | MPa | ISO 527-2/1A/50 |
| 拉伸應變 (屈服) | 7.0 | % | ISO 527-2/1A/50 |
| 標稱拉伸斷裂應變 | 16 | % | ISO 527-2/1A/50 |
| 拉伸蠕變模量 | ISO 899-1 | ||
| 1 hr | 2100 | MPa | ISO 899-1 |
| 1000 hr | 1200 | MPa | ISO 899-1 |
| 彎曲模量 (23°C) | 2400 | MPa | ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 簡支梁缺口沖擊強度 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m2 | ISO 179/1eA |
| 23°C | 4.0 | kJ/m2 | ISO 179/1eA |
| 簡支梁無缺口沖擊強度 | ISO 179/1eU | ||
| -30°C | 60 | kJ/m2 | ISO 179/1eU |
| 23°C | 60 | kJ/m2 | ISO 179/1eU |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 熱變形溫度 (1.8 MPa, 未退火) | 98.0 | °C | ISO 75-2/A |
| 熔融溫度 1 | 166 | °C | ISO 11357-3 |
| 線形熱膨脹系數 - 流動 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 注射 | 額定值 | 單位制 | |
|---|---|---|---|
| 干燥溫度 | 80.0 到 100 | °C | |
| 干燥時間 | 3.0 | hr | |
| 料筒后部溫度 | 176 | °C | |
| 料筒中部溫度 | 182 | °C | |
| 料筒前部溫度 | 188 | °C | |
| 射嘴溫度 | 198 | °C | |
| 加工（熔體）溫度 | 180 到 200 | °C | |
| 模具溫度 | 80.0 到 120 | °C | |
| 注塑壓力 | 60.0 到 120 | MPa | |
| 注射速度 | 慢 | ||
| 保壓 | 60.0 到 120 | MPa | |
| 背壓 | 0.00 到 0.500 | MPa |